Effect of BN content on the mechanical and dielectric properties of porous BNp/Si3N4 ceramics.
- Source :
-
Ceramics International . Jan2016 Part A, Vol. 42 Issue 1, p661-665. 5p. - Publication Year :
- 2016
-
Abstract
- Porous BN p /Si 3 N 4 ceramics were prepared by gas pressure sintering method as a candidate wave-transparent material. The effects of BN particle additions ranging from 0 wt% to 15 wt% on the phase compositions, microstructures, mechanical performance and dielectric properties were investigated. With the increase of BN content, the apparent porosity of the BN/Si 3 N 4 ceramics increased greatly from 2.3% to 21.2%. Although the mechanical properties were partially weaken, the dielectric performance of the porous BN/Si 3 N 4 was largely enhanced at the same time. For the 10% BN/Si 3 N 4 porous composite ceramics, the permittivity and dielectric loss was 33.5% and 62.2% lower than that of the porous Si 3 N 4 without BN content, respectively. Specifically, when 10% BN particles were added, the porous BN p /Si 3 N 4 has a porosity of 20.5% and the permittivity and dielectric loss were 5.14 and 0.0085 respectively with bending strength of 190.1 MPa and fracture toughness of 4.16 MPa m 1/2 , which can meet the required value of wave transparent materials. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 42
- Issue :
- 1
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 110681583
- Full Text :
- https://doi.org/10.1016/j.ceramint.2015.08.162