In situ production of ultra-fine Ti(C,N)–TiB2–Co cermets by reactive hot processing from the Co–Ti–C–BN system.
- Source :
-
International Journal of Refractory Metals & Hard Materials . Feb2016, Vol. 55, p1-10. 10p. - Publication Year :
- 2016
-
Abstract
- In this paper, ultra-fine Ti(C,N)–TiB 2 –Co cermets were prepared by reactive hot processing from the Co–Ti–C–BN system. Microstructure observation indicated that Co and TiB 2 uniformly distributed in the ultra-fine Ti(C,N) matrix. Carbon contents in the reactants had a great influence on the porosity and properties of synthesized cermets. In the range of 11.76–13.79 at.% carbon, dense samples were obtained. With increasing carbon contents, the relative density and hardness decreased due to the existence of residual carbon. The wear resistance of dense Ti(C,N)–TiB 2 –Co cermets were better than that of YT15 cemented carbide. In addition, the reaction process in the Co–Ti–C–BN system was explored by differential scanning calorimeter and X-ray diffraction. Results revealed that Ti(C,N) was synthesized through the solid solution of carbon into TiN, and the addition of Co to Ti–C–BN mixtures promoted the production of Ti(C,N) by the formation of Co–Ti liquid. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02634368
- Volume :
- 55
- Database :
- Academic Search Index
- Journal :
- International Journal of Refractory Metals & Hard Materials
- Publication Type :
- Academic Journal
- Accession number :
- 111828387
- Full Text :
- https://doi.org/10.1016/j.ijrmhm.2015.11.003