Effects of annealing on the color, absorption spectra, and light yield of Ce:YAlO[sub 3] single crystal grown by the temperature gradient technique.

YAlO[sub 3] single crystal doped with Ce[sup 3+] at concentration 1% was grown by the temperature gradient technique. The as-grown crystal was pink. After H[sub 2] annealing or air annealing at 1400 °C for 20 h, the crystal was turned into colorless. We concluded there were two kinds of color centers in the as-grown crystal. One is F[sup +] center attributed to absorption band peaking at about 530 nm, the other is O[sup -] center attributed to absorption band peaking at about 390 nm. This color centers model can be applied in explaining the experiment phenomena including the color changes, the absorption spectra changes, and the light yield changes of Ce:YAP crystals before and after annealing. © 2004 American Institute of Physics. [ABSTRACT FROM AUTHOR]