Effects Of Fine Alumina Dispersion On Ionic Conductivity And Mechanical Properties Of Ytterbia Stabilized Cubic Zirconia.
- Source :
-
Materials Research Innovations . Jun2004, Vol. 8 Issue 2, p115-120. 6p. - Publication Year :
- 2004
-
Abstract
- Nanocomposites of Yb2O3stabilized ZrO2(YbSZ) containing fine Al2O3dispersions were fabricated by conventional powder mixing and a pressureless sintering technique. A fine homogeneous microstructure was obtained for the composites. This microstructural refinement decreased the size of defects in the composites, which significantly increased the fracture strength of the composites compared to that of monolithic ZrO2. The composites had the same ionic conductivity values as those of the monolithic ceramics at high temperatures (in the range of 800–1000 °C). Furthermore, the activation energy at high temperatures was independent of the Al2O3content, whereas in the lower temperature regime (300–800 °C), it varied with the Al2O3fraction. This indicated that different O2-conduction-based activation processes were operating in the two temperature regimes. The O2-ion transfer could easily occur at high temperatures due to the presence of the Al2O3particulate dispersion in the composite system. From these results, it was concluded that the dispersion of fine grained Al2O3into YbSZ is advantageous for achieving high-strength ion-conductive cubic zirconia. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 14328917
- Volume :
- 8
- Issue :
- 2
- Database :
- Academic Search Index
- Journal :
- Materials Research Innovations
- Publication Type :
- Academic Journal
- Accession number :
- 118764061
- Full Text :
- https://doi.org/10.1080/14328917.2004.11784840