Low temperature pressureless sintering of dense silicon nitride using BaO-Al2O3-SiO2 glass as sintering aid.

Dense Si 3 N 4 ceramic with BaO-Al 2 O 3 -SiO 2 low temperature glass powders as sintering aids were prepared by pressureless sintering techniques at a relatively low temperature (1550 °C). Four kinds of glass powders of compositions melting at 1120 °C, 1300 °C, 1400 °C and 1500 °C, respectively, have been introduced as sintering aids. XRD results demonstrate that the BaO-Al 2 O 3 -SiO 2 glass powders reacted with BaAl 2 O 4 and converted into hexagonal celsian, which is a high-temperature phase with melting point of 1760 °C, so being beneficial to the high temperature properties of the materials. In addition, a portion of α-Si 3 N 4 transformed to rod like β-Si 3 N 4 with high aspect ratio as shown by XRD and SEM analysis. The bulk density increased with the rise of the melting temperature of the BaO-Al 2 O 3 -SiO 2 glass powders, the sample obtained with the BaO-Al 2 O 3 -SiO 2 glass powder melting at 1500 °C reaching a maximum density of 98.8%, an high flexural strength (373 MPa) and a fracture toughness (4.8 MPa m 1/2 ). [ABSTRACT FROM AUTHOR]