Surface modification effects on coercivity of the CoFe2O4 thin films with different thickness La0.7Sr0.3MnO3 layers.

High coercivity CoFe2O4 (CFO) thin films with large-area are very desirable for applications. Here, we report La0.7Sr0.3MnO3 (LSMO) layer decoration effects on coercivity in CFO thin films by solution processing. With LSMO layer decoration, the coercivity increases initially and then decreases with increasing LSMO layer thickness. Strain induced by the mismatched thermal expansion coefficient and magnetostrictive coefficient as well as the interfacial magnetic exchange coupling between CFO and LSMO are investigated. The room temperature out-of-plane and in-plane coercivity reached 7.6 and 4.9 kOe, respectively, are obtained, which are the highest values in solution derived CFO thin films. The improved coercivity is beneficial for applications and provides a facile route to enhance coercivity of CFO thin films through surface modification by soft magnetic layers. [ABSTRACT FROM AUTHOR]