Electrical and Electrochemical Studies on Sodium Ion-based Gel Polymer Electrolytes.

Gel polymer electrolytes (GPEs) have captured great attention because of their unique properties such as good mechanical stability, high flexibility and high conductivity approachable to that of the liquid electrolytes. In this work, we have prepared sodium ion conducting gel polymer electrolyte (GPE) films consisting of polyvinylidenefluoride-cohexafluoropropylene (PVdF-HFP) as a polymer host using the solution casting technique. Sodium trifluoromethanesulfonate (NaCF3SO3) was used as an ionic salt and the mixture of ethylene carbonate (EC) and propylene carbonate (PC) as a plasticizing solvent. Impedance spectroscopy measurements were carried out to determine the ionic conductivity of the GPE films. The sample containing 20 wt.% of NaCF3SO3 salt exhibits the highest room temperature ionic conductivity of 2.50 x 10-3 S cm-1. The conductivity of the GPE films was found to depend on the salt concentration that added to the films. The ionic and cationic transference numbers of GPE films were estimated by DC polarization and the combination of AC and DC polarization method, respectively. The results had shown that both ionic and cationic transference numbers are consistent with the conductivity studies. The electrochemical stability of the GPE films was tested using linear sweep voltammetry (LSV) and the value of working voltage range appears to be high enough to be used as an electrolyte in sodium batteries. The cyclic voltammetry (CV) studies confirmed the sodium ion conduction in the GPE films. [ABSTRACT FROM AUTHOR]