Synergistic effects of ion doping and surface-modifying for lithium transition-metal oxide: Synthesis and characterization of La2O3-modified LiNi1/3Co1/3Mn1/3O2.

It is highly desirable to improve the high voltage stabilities of cathode materials for Li-ion battery materials since it can deliver a higher reversible capacity at high cutoff voltage. Herein, we propose a novel facile strategy to generate La 2 O 3 -modified LiNi 1/3 Co 1/3 Mn 1/3 O 2 with superior electrochemical performance in the voltage range of 2.5–4.5 V via a solid-state method. It can be observed that La 2 O 3 -modified LiNi 1/3 Co 1/3 Mn 1/3 O 2 can greatly enhance the electrochemical performance due to the synergistic effect of ion doping and surface-modifying. La ions doping can alleviate the Li + /Ni 2+ mixing, and substantially enhance the structure stability of LiNi 1/3 Co 1/3 Mn 1/3 O 2 during charge/discharge cycles at high cutoff voltage. LaNi 0.4 Co 0.6 O 3 /LaMnO 3.26 spreading on the surface layer is very useful in improving the diffusion of Li + and inhibiting the particles from reacting with the electrolyte, enhancing the high voltage stabilities of the interface between electrode and electrolyte. The capacity retention of 0.7% (molar fraction) La 2 O 3 -modified LiNi 1/3 Co 1/3 Mn 1/3 O 2 is 79.0% after 300 cycles compared to 61.7% for bare LiNi 1/3 Co 1/3 Mn 1/3 O 2 . And its discharge capacity at 10 C is 141.7 mAh g −1 in the voltage range of 2.5–4.5 V, which is higher than those of other samples. This work not only offers a facile novel strategy to achieve superior electrochemical performances of cathode materials but also presents some new insights into the stabilization mechanism of modified cathode materials during charge/discharge cycles or long-term storage at high cutoff voltage. [ABSTRACT FROM AUTHOR]