Spark plasma sintering and mechanical properties of compounds in TiB2-SiC pseudo-diagram.
- Source :
-
Ceramics International . Dec2018, Vol. 44 Issue 18, p22357-22364. 8p. - Publication Year :
- 2018
-
Abstract
- Abstract The influence of spark plasma sintering (SPS) parameters (temperature, time, pressure) and the role of particle size on densification, microstructure and mechanical properties of commercial additive-free TiB 2 , SiC and composites thereof were studied by X-ray diffraction, scanning electron microscopy, the ultrasonic method and indentation. Three particle sizes of SiC and 2 of TiB 2 were processed. An optimal cycle was found for TiB 2 and SiC: 2000 °C, 3 min dwell time, and 100 MPa applied at 600 °C. The relative density of pure SiC increases linearly from 70% to 90% when the initial particle size decreases from 1.75 µm to 0.5 µm. Pure TiB 2 was densified up to 87%. Using 2.5 wt% SiC in TiB 2 , the relative density increases to 97%. Young's modulus and the hardness of all samples were measured, with results discussed. The higher properties were obtained for additive-free TiB 2 –5%SiC with a relative density of 97% and with the Young's modulus and Vickers hardness values being close to 378 GPa and 23 GPa, respectively. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 44
- Issue :
- 18
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 132690114
- Full Text :
- https://doi.org/10.1016/j.ceramint.2018.08.362