Design, microstructure and high temperature properties of in-situ Al3Ti and nano-Al2O3 reinforced 2024Al matrix composites from Al-TiO2 system.

Abstract This study was conducted to obtain a type of aluminum matrix composites exhibiting a good strength and certain ductility at high temperature. The 25 vol% TiO 2 -75 vol%2024 Al systems were selected to fabricate the (Al 3 Ti+Al 2 O 3)/2024 Al composites with residual ∼32 vol% Al matrix through powder metallurgy. The (Al 3 Ti+Al 2 O 3)/2024 Al exhibits a good strength and certain ductility at high temperature as in the design. The microstructure of (Al 3 Ti+Al 2 O 3)/2024 Al composites was investigated. It was discovered that the in-situ Al 3 Ti reinforcement was in coarse block-shaped particles of approximately 6.9 μm in size and the Al-Al 3 Ti interface was clean. The Al 2 O 3 particles were in the nano-scale and distributed in the Al matrix in a cluster form. The high temperature compression testing of the composites was conducted at the temperatures of 573 K, 623 K, 673 K, 723 K and 773 K with the strain rate of 10−3 ∼ 0.42 s−1. The results demonstrated that the composites exhibited higher strength at the same high temperature than the other Al matrix composites with a similar volume fraction. The massive Al 3 Ti and Al 2 O 3 phases played a load bearing role at high temperatures. The residual ∼32 vol% Al matrix led the composites to acquire certain ductility. Graphical abstract Image 1 Highlights • In-situ (Al 2 O 3 +nano-Al 2 O 3)/2024 Al composites were produced by TiO 2 and 2024 Al. • The composites exhibited high strength properties between 573 K-773 K. • The composites exhibited a certain ductility for residual ∼32 vol% Al matrix. [ABSTRACT FROM AUTHOR]