Diode-pumped continuous-wave a- and c-cut Pr:Sr0.5La0.5Mg0.5Al11.5O19 (Pr:ASL) visible lasers at 645 and 726 nm.
- Source :
-
Journal of Alloys & Compounds . Jul2019, Vol. 792, p1200-1205. 6p. - Publication Year :
- 2019
-
Abstract
- Pr3+-doped Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 (ASL) crystal along 〈100〉 direction was successfully grown using the Czochralski technique under azote atmosphere. Absorption and emission spectra of Pr:ASL crystal have been measured at room temperature. Continuous-wave laser operation of the a-cut and c-cut Pr:ASL samples under InGaN laser diode pumping has been demonstrated. For deep red laser operation at about 726 nm, the maximum output powers achieved from a-cut sample was 92.8 mW with slope efficiency of about 11.9%, while 46.6 mW with slope efficiency of 8.0% for the c-cut sample. For red laser at about 645 nm, maximum output powers of 49.2 mW and 42.8 mW were obtained for the a-cut sample and c-cut sample, corresponding to a slope efficiency of 6.7% and 8.5%, respectively. • Pr:Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 crystal was successfully grown using the Czochralski method. • Spectral parameters of Pr:Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 crystal were obtained. • Red and deep red laser were demonstrated in Pr:Sr 0.5 La 0.5 Mg 0.5 Al 11.5 O 19 crystal. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 09258388
- Volume :
- 792
- Database :
- Academic Search Index
- Journal :
- Journal of Alloys & Compounds
- Publication Type :
- Academic Journal
- Accession number :
- 136271541
- Full Text :
- https://doi.org/10.1016/j.jallcom.2019.04.125