Fine-grained processing and electron backscatter diffraction (EBSD) analysis of cold-rolled Inconel 617.
- Source :
-
Journal of Alloys & Compounds . Aug2019, Vol. 799, p302-313. 12p. - Publication Year :
- 2019
-
Abstract
- Fine-grained processing of Inconel 617 sheet was proposed, and microstructural evolution during processing was analyzed. The optimum recovery temperature at 750 °C and the best recrystallization annealing temperature at 1000 °C were determined by experiments. The optimal fine-grained process comprised heat treatment (750 °C × 1 h), first cold rolling (60% reduction rate), high-temperature recovery (750 °C × 1 h), second cold rolling (10% reduction rate), and recrystallization annealing (1000 °C × 3 h). After recrystallization annealing (1000 °C × 3 h), the fine-grained sheet consisted of equiaxed grains with a size of 4–6 μm. A high proportion of high-angle grain boundaries was observed, and most of the grain orientation spread values were less than 1. The grain recrystallized completely. Twin refinement mechanism played a dominant role in sheet grain refinement. The hardness and tensile mechanical properties of the fine-grained sheet were notably stronger than those of the original sheet. • A new grain refinement process for an Inconel 617 sheet was proposed. • A fine-grained sheet with an average grain size of 4–6 μm was prepared. • Fine-grained sheet was analyzed by EBSD. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 09258388
- Volume :
- 799
- Database :
- Academic Search Index
- Journal :
- Journal of Alloys & Compounds
- Publication Type :
- Academic Journal
- Accession number :
- 137051581
- Full Text :
- https://doi.org/10.1016/j.jallcom.2019.05.193