Synthesis and characterization of activated 3D graphene via catalytic growth and chemical activation for electrochemical energy storage in supercapacitors.
- Source :
-
Electrochimica Acta . Nov2019, Vol. 324, pN.PAG-N.PAG. 1p. - Publication Year :
- 2019
-
Abstract
- Activated three-dimensional graphene (3D-AGE) powders with high specific surface area have been successfully prepared by combined strategies of catalytic growth and chemical activation for application in supercapacitors. The morphology, structure and composition of 3D-AGE are investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), nitrogen adsorption-desorption and X-ray photoelectron spectroscopy (XPS). The electrochemical performance is evaluated by cyclic voltammetry (CV), galvanostatic charge-discharge (GDC) and electrochemical impedance spectroscopy (EIS). The results show that the 3D-AGE exhibits very high specific capacitance and stability as electrode material for supercapacitor in 1 mol L−1 KOH aqueous electrolyte. It is found that at a current density of 1 A g−1, the specific capacitance of 3D-AGE is 258.2 F g−1, which is much higher than the one (87.8 F g−1) of pristine 3D graphene (3D-GE). It is also found that after 2000 charge-discharge cycles, the specific capacitance increases from 285.2 to 345.3 F g−1, with an impressive increment rate of up to 21%. The excellent electrochemical performance of 3D-AGE can be attributed to its unique 3D nanostructure with high surface area, abundant oxygen functional groups, as well as fast ion and electron transport rates. Image 108229 • Newly three-dimensiona activated graphene (3D-AGE) with high specific surface area was fabricated. • Catalytic growth and chemical activation were employed for 3D-AGE powder material preparation. • The as prepared 3D-AGE is apropriate for electrochemical energy storage in supercapacitors. • At a current density of 1 A g-1, the specific capacitance of 3D-AGE is 258.2 F g-1. • After 2000 charge-discharge cycles, the specific capacitance increases from 285.2 to 345.3 F g-1. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00134686
- Volume :
- 324
- Database :
- Academic Search Index
- Journal :
- Electrochimica Acta
- Publication Type :
- Academic Journal
- Accession number :
- 139120808
- Full Text :
- https://doi.org/10.1016/j.electacta.2019.134878