Layered hydroxide/polydopamine/hyaluronic acid functionalized magnesium alloys for enhanced anticorrosion, biocompatibility and antithrombogenicity in vascular stents.

Magnesium alloys are promising cardiovascular stent materials due to the favourable physical properties and complete biodegradability in vivo. However, the rapid degradation, poor cytocompatibility and tendency of thrombogenesis hinder practical clinical applications. In order to solve these problems, a facile and highly efficient strategy of alkali treatment combined with subsequent layer-by-layer assembly was used to fabricate a multifunctional coating. A bottom layer hydroxyl (–OH) with negative charge after alkali treatment first formed a solid bond with magnesium matrix to provide a rough outer surface for the further immobilization of functional biomolecules. Afterwards, polydopamine and hyaluronic acid were successively immobilized on alkali-treated magnesium surface via strong electrostatic adsorption and covalent bonding between carboxyl group of hyaluronic acid and amine or hydroxyl of polydopamine to form magnesium/OH/polydopamine/hyaluronic acid. Hydroxyl significantly improves the corrosion resistance while polydopamine and hyaluronic acid layers act as a further barrier to provide better anticorrosion. A balance between biocompatibility and antithrombogenicity has been achieved by adjusting the content of hyaluronic acid on polydopamine surface. The multifunctional magnesium/OH/polydopamine/hyaluronic acid coating with lower hyaluronic acid concentrations expose more active sites of polydopamine molecules to promote endothelial cell proliferation while retaining the intrinsic antithrombogenic function of hyaluronic acid to offer a potential application for vascular stents. [ABSTRACT FROM AUTHOR]