Enhanced storage energy density and fatigue free properties for 0.94Bi0.50(Na0.78K0.22)0.50Ti1-x(Al0.50Nb0.50)xO3-0.06BaZrO3 ceramics.
- Source :
-
Ceramics International . Jul2020:Part B, Vol. 46 Issue 10, p17044-17052. 9p. - Publication Year :
- 2020
-
Abstract
- The high storage energy density (W rec) and conversion efficiency (η) for lead-free ceramics have been attained significant interest in recent times for electronic devices. Enhanced W rec and stable fatigue properties are examined for lead-free 0.94Bi 0·50 (Na 0·78 K 0.22) 0.50 Ti 1- x (Al 0·50 Nb 0.50) x O 3 -0.06BaZrO 3 (for 0 ≤ x ≤ 0.05) ceramics, synthesized using the solid-state reaction method. Crystal structure and lattice dynamics are revealed by the X-ray diffraction and Raman scattering techniques. Highly compact ceramics is obtained with decreasing average grain size from 0.94 ± 0.23 μm (for x = 0) to 0.76 ± 0.31 μm (for x = 0.05) as a function of composition. A high W rec ~1.32 J/cm3 and η ~76.60% is achieved for x = 0.04 ceramic at room temperature with applied 95 kV/cm. In addition, W rec ~1.40 J/cm3 and η ~86% are perceived with a 90 kV/cm at 80 °C. Also, it is obtained as a fatigue-free property for x = 0.04 composition ceramic up to 105 cycles. Hence, this improvement in energy density performance and stable fatigue resistance for x = 0.04 dielectric ceramic is expected for practical applications in many electronic appliances. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 46
- Issue :
- 10
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 143192425
- Full Text :
- https://doi.org/10.1016/j.ceramint.2020.03.292