One-pot synthesis of hierarchical Co1–xS/NC@MoS2/C hollow nanofibers based on one-dimensional metal coordination polymers for enhanced lithium and sodium-ion storage.

Multicomponent metal sulfides have been recognized as promising anode materials for lithium/sodium-ion storage given their enticing theoretical capacities. However, the simplification of synthetic processes and the construction of heterogeneous interfaces of multimetal sulfides remain great challenges. Herein, a hierarchical 1T-MoS 2 /carbon nanosheet decorated Co 1– x S/N-doped carbon (Co 1– x S/NC@MoS 2 /C) hollow nanofiber was designed and constructed via a one-pot hydrothermal method using a cobalt-based coordination polymer nanofiber. This nanofiber can transform in-situ into conductive N-doped carbon hollow fibers embedded with active Co 1– x S nanoparticles, enabling the epitaxial growth of MoS 2 nanosheets. Consequently, the Co 1– x S/NC@MoS 2 /C composites achieve exceptional lithium/sodium-ion storage performance. Compared to MoS 2 /C microspheres and Co 1– x S/NC hollow nanofibers alone, the Co 1– x S/NC@MoS 2 /C hollow nanofibers deliver higher discharge capacities (1085.9 mAh g−1 for lithium-ion batteries (LIBs) and 748.5 mAh g−1 for sodium-ion batteries (SIBs) at 100 mA g−1), better capacity retention (910 mAh g−1 for LIBs and 636.5 mAh g−1 for SIBs after 150 cycles at 100 mA g−1), and increased cycling stability (407.2 mAh g−1 after 1000 cycles for SIBs at 1000 mA g−1). Furthermore, the kinetic analysis shows that the lithium/sodium-ion storage processes of the Co 1– x S/NC@MoS 2 /C electrode are mainly controlled by pseudocapacitance behavior. The excellent electrochemical properties can thus be ascribed to the synergy of the MoS 2 /C nanosheets with the enlarged interlayer spacing, good conductivity of the carbon layers, and the Co 1– x S nanoparticles embedded in the hollow nanofibers with extensive reaction sites. [ABSTRACT FROM AUTHOR]