Erratum: Growth of TlBa2Ca2Cu3O9 Epitaxial Thin Films by Two-Step Method in Argon [Chin. Phys. Lett. 36 (2019) 057401].

The corresponding description of this figure should be "As shown in Fig.2, the full width at half maximum (FWHM) of the Tl-1223(006) reflection peak is only 0.58 , which shows that the film possesses a good crystalline structure", instead of "As shown in Fig.2, the FWHM of the Tl-1223(003) reflection peak is only 0.58 , which shows that the film possesses a good crystalline structure". 36(2019)057401] Jian Xing( ) 1, Li-Tian Wang( ) 1, Xiao-Xin Gao( ) 1, Xue-Lian Liang( ) 1, Kai-Yong He( ) 1, Ting Xue( ) 1, Sheng-Hui Zhao( ) 1, Jin-Li Zhang( ) 1, Ming He( ) 1,2, Xin-Jie Zhao( ) 1,3, Shao-Lin Yan( ) 1, Pei Wang( ) 4, and Lu Ji( ) 1,3* 1 College of Electronic Information and Optical Engineering, Nankai University, Tianjin 300350, China 2 Tianjin Key Laboratory of Optoelectronic Sensor and Sensing Network Technology, Tianjin 300350, China 3 Key Laboratory of Photoelectronic Thin Film Devices and Technology of Tianjin, Tianjin 300350, China 4 Beijing Institute of Radio Measurement, Beijing 100854, China (Received 26 October 2020; accepted 18 December 2020; published online 27 January 2021) DOI: 10.1088/0256-307X/38/2/029901 1 4 1 6 1 8 2 0 0. 0 1. 5 3. 0 4. 5 6. 0 I n t e n s i t y (1 0 4 c p s) w (d e g) F W H M = 0. 5 8 O Fig. In Fig.2 of the article, [1] the figure caption should be"Rockingcurveofthe(006)peakoftheTl-1223thin film" instead of "Rocking curve of the (003) peak of the Tl-1223 thin film". [Extracted from the article]