Effects of Zn substitution on high-frequency properties of Ba1.5Sr1.5Co2-xZnxFe22O41 hexaferrites.
- Source :
-
Ceramics International . Jun2021, Vol. 47 Issue 12, p17120-17127. 8p. - Publication Year :
- 2021
-
Abstract
- Ba 1.5 Sr 1.5 Co 2-x Zn x Fe 22 O 41 (x = 0,0.4,0.8,1.2,1.6,2.0) hexaferrites substituted by Zn were prepared via conventional solid-state reaction. The influences of Zn substitution content on phase formation, microstructure, and magnetic properties, especially high-frequency magnetic properties, were systematically investigated. Results indicate that, when sintering temperature is 1200 °C, pure ferrite phase of Co 2 Z is formed, and Zn2+ is successfully incorporated into the lattice. Appropriate amount of Zn substitution can improve the densification and saturation magnetization (M s) of Z-type ferrite, thereby effectively promoting permeability. However, due to limitations of Snoek's law, cut-off frequency is found to be reduced with Zn substitution. For x = 0.4, the sample exhibits both high permeability (up to 22.49) and high cut-off frequency (~900 MHz), with Snoek constant (μ i − 1) × f r reaching 19.337 GHz. Furthermore, magnetic loss for the sample with x = 0.4 is found to be low. It is anticipated that this material will have extensive application prospects for miniaturization and high frequency antenna applications. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 47
- Issue :
- 12
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 150185536
- Full Text :
- https://doi.org/10.1016/j.ceramint.2021.03.021