In situ formation of SiC in Al–40Si alloy during high-pressure solidification.

The in situ formation of SiC in Al–40Si alloys during the fabrication of SiC/Al–Si composites by high-pressure solidification were investigated. The results demonstrate that the in situ formation of SiC occurs by a gradual conversion of Al 4 C 3 and Al 4 SiC 4 to SiC. In situ SiC can be formed in an Al–40Si alloy solidified under a pressure of 3 GPa at a temperature of 1373 K. The SiC particles (SiC p) formed in situ was compatible with the α-Al matrix and the Si phases. The relative density of the SiC/Al-38.6Si composite was 99.9%. The bending strengths of the Al–40Si alloy and the SiC/Al-38.6Si composite obtained by solidification under a pressure of 3 GPa were 200.8 MPa and 322 MPa, respectively, which represents an enhancement of 60.3% as a result of reinforcement by the in situ-formed SiC. [ABSTRACT FROM AUTHOR]