Spectral properties and laser operation of Nd3+-doped mixed sesquioxide LuYO3 ceramic.

The absorption spectrum, fluorescence spectrum and fluorescence time of a mixed sesquioxide Nd:LuYO 3 ceramic were measured at room temperature. Judd-Ofelt theory was applied to calculate the spectral parameters of Nd:LuYO 3. The absorption cross section at 812 nm was calculated to be 0.99 × 10−20 cm2 with full width at half maximum (FWHM) of 47.69 nm. The emission cross-section at 1077 nm was calculated to be 5.24 × 10−20 cm2 with FWHM of 11.62 nm. The fluorescence lifetime and quantum efficiency of the 4F 3/2 multiplet were determined to be 228.4 μs and 85.2%, respectively. Continuous-wave (CW) laser operation of Nd:LuYO 3 ceramic was demonstrated. Simultaneous laser operation at 1075.24 and 1080.03 nm was achieved with maximum output power of 490 mW and slope efficiency of 6.36%. • Nd:LuYO3 ceramic was fabricated by solid-state reaction. • Judd-Ofelt theory was used to analyze the spectroscopic properties of Nd:LuYO 3 ceramic. • CW laser operation was performed and output power of 490 mW at the absorbed power of 9.1 W is obtained. [ABSTRACT FROM AUTHOR]