Effect of the molecular weight of poly(vinyl acetate) on the polymorphism and thermomechanical properties of poly(L-lactic acid)/poly(D-lactic acid) blends.

The effects of molecular weight (Mw) and content of poly(vinyl acetate) (PVAc) on the crystallization behaviors, competing crystallization of homocrystallites and stereocomplex crystallites (SCs), crystalline structure, and mechanical properties of poly(L-lactic acid) (PLLA)/poly(D-lactic acid) (PDLA) blends were investigated. The crystallization of PLLA/PDLA component is accelerated after the addition of low-Mw PVAc and is suppressed with high-Mw PVAc. The ability of SC formation is enhanced via blending with PVAc, irrespective of its Mw, and becomes prominent with low-Mw PVAc. The exclusive SCs are obtained in the blends with 30 mass % low-Mw PVAc. The improvement in thermomechanical property above 170 °C is ascribed to the enhancement of SC content. This work presents guidance for achieving the melt processability of SC-PLA, thus proving their potential as a high-performance substitute for conventional plastics. [ABSTRACT FROM AUTHOR]