Growth, spectroscopy and CW laser operation of Ho3+ doped CaY0.9Gd0.1AlO4 single crystal.

Ho3+-doped CaY 0.9 Gd 0.1 AlO 4 single crystal was successfully grown by the Czochralski technique for the first time. The polarized absorption spectra, polarized luminescence spectra and fluorescence decay curve of the crystal were investigated at room temperature. The spectroscopic parameters are calculated based on Judd–Ofelt theory, the values of Ω 2,4,6 were calculated to be 3.16 × 10−20 cm2, 3.93 × 10−20 cm2, 0.91 × 10−20 cm2, respectively. The Ho:CaY 0.9 Gd 0.1 AlO 4 crystal exhibits strong emission at 2013 nm for π- and 2032 nm for σ-polarizations with stimulated emission cross section of 6.64 × 10−20 cm2 and 1.90 × 10−20 cm2, respectively. The fluorescence lifetime of the 5I 7 level was measured to be 6.60 ms. The continuous-wave (CW) laser operation of Ho:CaY 0.9 Gd 0.1 AlO 4 crystal around 2 μm was demonstrated. • Ho3+-doped CaY 0.9 Gd 0.1 AlO 4 single crystal was successfully grown by the Czochralski technique for the first time. • The emission cross-section at 2013 nm and 2032 nm are 6.64 × 10−20 cm2 and 1.90 × 10−20 cm2 for π- and σ-polarizations respectively. • The continuous-wave (CW) laser operation of Ho:CaY 0.9 Gd 0.1 AlO 4 crystal around 2 μm was demonstrated. [ABSTRACT FROM AUTHOR]