Microstructure and Erosion Wear Characterization of a New Cast High-Vanadium–Chromium Alloy (HVCA).

To evaluate the enhanced erosion wear performance under acidic medium, a new high-vanadium–chromium alloy (HVCA) is designed and test samples produced by sand casting. The microstructure was analyzed by SEM, TEM and XRD. The erosion wear performance was tested in acidic medium designed by orthogonal test method. The factors affecting the erosion wear performance of HVCA are analyzed. The research results show that microstructure of HVCA is characterized by different carbides (M7C3, M23C6, VC, M2C) distributed in martensite and residual austenite. The hardness is 65.16 ± 0.2 HRC, and the impact toughness is 9.82 ± 0.12 J/cm2. H2SO4 concentration has the greatest influence on the erosion wear performance of HVCA, followed by the erosion wear angle. The maximum erosion wear performance of HVCA is 1.59 times that of HCCI. Compared with HCCI, HVCA has excellent erosion wear resistance because of its high hardness and toughness, a small amount of fracture and carbide shedding, and slight corrosion and wear interaction under erosion wear condition. [ABSTRACT FROM AUTHOR]