Influence of Gd2O3 on the microstructure and properties of transparent MgAl2O4: Cr3+ ceramic.

In this work, MgAl 2 O 4 : Cr3+ transparent ceramics have been synthesized by the hot press sintering techniques, and the effect of the sintering aid Gd 2 O 3 and its content on the densification, microstructure, and optical, photoluminescence was studied and discussed. The relative density reached 99.29% with 0.8 wt% Gd 2 O 3 as a sintering aid, and the optical transmittance at 686 nm and 1446 nm were approximately 76%. As Gd 2 O 3 content continued to increase, the grain size of the ceramics became smaller and uniform, accompanied by some pores with the size of ～1 μm. The ceramics with 4.0 wt% Gd 2 O 3 showed a higher transmittance, of 82% at 1446 nm. Additionally, Gd 2 O 3 was helpful for Cr3+ in the sites of octahedral symmetry, which increased the quantum yield. The quantum yield of MgAl 2 O 4 : Cr3+ with 0.8 wt% Gd 2 O 3 was about 0.175, which was 36% higher than that of ceramic without Gd 2 O 3. In short, the sintering aid Gd 2 O 3 not only contributed to improving the densification, homogenizing the grain size, and heightening the optical transmittance but also enhanced the quantum yield of Cr3+. [ABSTRACT FROM AUTHOR]