Rapid hardening response of ultra-hard Ti-6Al-2Sn-4Zr-6Mo alloy produced by laser powder bed fusion.

Post heat treatment is essential for additively manufactured alloys to eliminate residual stress and in some cases further improve mechanical performance. This study systematically investigated the hardening response of a Ti-6Al-2Sn-4Zr-6Mo alloy processed by laser powder bed fusion (LPBF) to a one-step heat treatment. The results revealed significant hardening at both 500 °C and 650 °C. Most notably, an ultra-high peak-hardness of 563VHN was achieved within 5 mins of heat treatment at 650 °C due to a unique martensite-decomposed α+β microstructure consisting of alternating long β laths that are ∼5 nm thick and α laths that are ∼35 nm thick, and within the α laths are also short β laths that are ∼2 nm thick with an ∼11 nm inter-spacing. The influence of both types of β laths on the α lath thickness was established and related to the ultra-high hardness observed, which provides new insight for the design of new metastable LPBF-processed Ti alloys. [Display omitted] [ABSTRACT FROM AUTHOR]