Oxidation behavior and kinetics of magnetron-sputtered Cr-coated Zr alloy cladding in 1000–1300 ℃ steam environment.
- Source :
-
Corrosion Science . Jul2023, Vol. 218, pN.PAG-N.PAG. 1p. - Publication Year :
- 2023
-
Abstract
- The isothermal oxidation behavior of magnetron-sputtered Cr-coated Zr-1Nb alloy cladding in 1000–1300 ℃ steam environment is studied. The phenomena at each temperature are summarized and the oxidation kinetics are discussed. Cr coating can maintain the oxidation resistance for more than 6 h at 1000 ℃ and 1100 ℃ under double-sided oxidation condition, while suffered degradation during long-duration oxidation at 1200 ℃ and 1300 ℃. After coating degradation, Zr substrate was oxidized prior to residual metallic Cr and the metallic Cr was not completely oxidized until the ZrO 2 layer beneath the coating had grown to a certain thickness. Mainly due to the redox reaction between Zr and Cr 2 O 3 and the preferential oxidation of Zr substrate, the thickness of Cr 2 O 3 film decreased after a certain oxidation duration. The Cr coating after degradation at 1200 ℃ can still hinder the oxidation of Zr substrate to a certain extent, while that at 1300 ℃ almost lost the protective effect. • Isothermal steam oxidation of Cr-coated Zr alloy was performed in temperature range of 1000–1300 ℃. • Oxidation kinetics of Cr-coated Zr alloy cladding was summarized. • Oxidation behavior of Zr substrate after coating degradation were discussed. [ABSTRACT FROM AUTHOR]
- Subjects :
- *OXIDATION kinetics
*OXIDATION-reduction reaction
*ALLOYS
*OXIDATION
*CHROMATES
Subjects
Details
- Language :
- English
- ISSN :
- 0010938X
- Volume :
- 218
- Database :
- Academic Search Index
- Journal :
- Corrosion Science
- Publication Type :
- Academic Journal
- Accession number :
- 163515795
- Full Text :
- https://doi.org/10.1016/j.corsci.2023.111215