Joining MgAl2O4 ceramics using ZnO–Al2O3–SiO2 glass ceramic with precipitated ZnAl2O4.
- Source :
-
Ceramics International . Oct2023, Vol. 49 Issue 20, p32835-32842. 8p. - Publication Year :
- 2023
-
Abstract
- In this work, crystallization, thermal expansion and wetting behavior of ZnO–Al 2 O 3 –SiO 2 (ZAS) glass were first investigated. The results showed that ZnAl 2 O 4 was precipitated from ZAS glass after crystallization treatment. Crystallization increased the coefficient of thermal expansion (CTE) of ZAS glass ceramic due to the high CTE of ZnAl 2 O 4. In addition, ZAS glass exhibited good wettability on the surface of MgAl 2 O 4 substrate. On this basis, ZAS glass was used to join MgAl 2 O 4 ceramic, and the microstructure and mechanical properties of joints obtained with different cooling methods were investigated. The flexural strength of joints was related to the content of ZnAl 2 O 4 crystals in the brazing seams. Additional nucleation and crystallization treatment during cooling process improved the crystallinity of brazing seam, resulting in better matching of the CTE of brazing seam with that of MgAl 2 O 4 ceramic. The maximum flexural strength of joints reached 201 MPa, which was equivalent to the strength of MgAl 2 O 4 ceramic. [ABSTRACT FROM AUTHOR]
- Subjects :
- *FLEXURAL strength
*GLASS
*THERMAL expansion
*BRAZING
*CERAMICS
*CRYSTALLIZATION
Subjects
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 49
- Issue :
- 20
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 171367939
- Full Text :
- https://doi.org/10.1016/j.ceramint.2023.07.254