Spectroscopic properties of Er3+-doped PbO–Ga2O3–GeO2 glass for optical amplifiers
- Source :
-
Optical Materials . Jan2005, Vol. 27 Issue 4, p679-690. 12p. - Publication Year :
- 2005
-
Abstract
- Abstract: The spectroscopic properties of Er2O3-doped PbO–Ga2O3–GeO2 glasses were investigated. The measured lifetime and stimulated emission cross-section of the 4I13/2 level were 4.73±0.05ms and 6.8×10−21 cm2, respectively. The measured lifetime and stimulated emission cross-section were 0.31±0.02ms and 1.9×10−21 cm2 for the 4I11/2 level, respectively. The lifetimes of 4I13/2 levels were almost constant up to the Er3+ concentration of ∼1.3×1020 cm−3. The constant α (6) for energy migration of the 4I13/2 level was considerably higher than that of the 4I11/2 level. On the other hand, the coefficient of cooperative upconversion for the 4I13/2 level was 104 times smaller than that for the 4I11/2 level at the concentration of 2.57×1020 cm−3. These results suggest that the contribution of the migration-accelerated energy transfer among Er3+ ions to the non-radiative transition from the 4I13/2 level is larger than that from the 4I11/2 level, whereas the non-radiative transition from the 4I11/2 level is mainly due to the cooperative upconversion effect via 4I11/2:4I11/2 → 4 F7/2:4I15/2 process. The obtained results also indicate that the PbO–Ga2O3–GeO2 glass is a good candidate for short optical fiber amplifiers. [Copyright &y& Elsevier]
- Subjects :
- *SPECTRUM analysis
*FIBER optics
*RADIATIVE transitions
*OPTICAL amplifiers
Subjects
Details
- Language :
- English
- ISSN :
- 09253467
- Volume :
- 27
- Issue :
- 4
- Database :
- Academic Search Index
- Journal :
- Optical Materials
- Publication Type :
- Academic Journal
- Accession number :
- 17250655
- Full Text :
- https://doi.org/10.1016/j.optmat.2004.04.018