Mechanical and thermal properties of Si3N4 ceramics prepared by gelcasting using high-solid-loading slurries.

In this study, according to the Dinger model, aqueous Si 3 N 4 slurries with a solid loading of 63 vol% and a viscosity lower than 1.0 Pa s were successfully prepared using two-grade Si 3 N 4 powders with D 50 = 7.2 μm and 9.4 μm as starting materials. These resulting slurries exhibited good rheological properties and suspension stability. Notably, the presence of β-Si 3 N 4 seeds existed in the starting materials effectively reduced the nucleation barrier by transforming homogeneous nucleation into heterogeneous nucleation. Consequently, it facilitated the reconstructive phase transformation of α-Si 3 N 4 to β-Si 3 N 4 , promoted the anisotropic growth of β-Si 3 N 4 nucleation, and resulted in the final formation of the bimodal microstructure. This unique microstructure significantly enhanced the mechanical properties of Si 3 N 4 ceramics, resulting in a high flexural strength of 1011.4 MPa and a fracture toughness of 14.8 MPa m1/2. These excellent properties were achieved through the combination of gelcasting and gas pressure sintering. Simultaneously, the Si 3 N 4 ceramics exhibited a low thermal conductivity of 47.7 W m−1 K−1, mainly owing to the low density of 95.3 %, the presence of low-thermal-conductivity silicate-based noncrystalline substances, and the possible existence of lattice oxygen in Si 3 N 4 crystals. [ABSTRACT FROM AUTHOR]