Effect of concentration of water-soluble phenolic resin on the properties of carbon paper for gas diffusion layer.

Carbon paper is one of the most widely used gas diffusion layer substrate materials due to its stable performance, relatively low cost, and easy for subsequent processing. Water-soluble phenolic resin, which is more ecologically friendly than alcohol-soluble phenolic resin, was used to prepare carbon paper as the precursor of the carbon matrix. And the effect of different resin solution concentrations on the properties of carbon paper was explored. The results showed that the graphitization, electrical conductivity and mechanical properties of carbon paper increased with the increase of resin solution concentration. When the concentration of resin solution was 20 wt%, the performance of carbon paper was relatively optimal. The graphitization of the carbon paper reached 65.45%, the porosity reached 80.74%, the resistance value at 1 MPa pressure was only 7.61 mΩ cm2, the tensile strength was 1.57 MPa, and the elastic modulus was 1210.98 MPa. [ABSTRACT FROM AUTHOR]