Effect of Cr2O3 Addition on Sintering Behavior of Novel Chromite‐Based Ladle Filler Sand.

Developing novel filler sands has garnered significant interest in improving the ladle's free‐opening rate and enhancing the cleanliness of high‐Mn and high‐Al steel. Laboratory studies explore the effect of adding Cr2O3 powder on the sintering behavior of chromite‐based filler sands. Furthermore, interfacial phenomena are examined between the sands and the steel grades, varying in Mn contents. The results demonstrate that adding Cr2O3 power plays a role in inhibiting the liquid phase formation in the sand. With a 16% addition, the steel (Mn mass% = 30) reacts with the sand, leading to the shape of a spinel phase, specifically (Mn, Fe, Mg)O·(Al, Cr)2O3, which facilitates the separation of the liquid phase. The reduction of FeO to Fe by Mn, Al, and C in steel, especially Al, is hindered by adding Cr2O3, resulting in a suitable sintering degree that ultimately benefits ladle free‐opening. SiO2 is crucial for forming the liquid phase during the sintering process. The SiO2 content of the sand should be about 20% to achieve optimal sintering effects. Chromite sand for casting is not suitable for the steels. The mixed sand presented in the current study demonstrates potential as a suitable filler sand for the steel (20 ≤ Mn mass% ≤ 30). [ABSTRACT FROM AUTHOR]