Coordinated regulation for α-Al2O3 and mullite structures in the alumina-mullite fiber based on the different adding form of Fe element.

The coordinated regulation for α-Al 2 O 3 and mullite structures in the alumina-mullite duplex fiber poses a challenging yet crucial task in achieving a fiber with exceptional high-temperature properties. In this study, Fe element was added into the alumina-mullite fibers in the form of iron sol and ferric nitrate solution, respectively, with the aim of obtaining a fiber consisting of fine mullite grains embedded with nano α-Al 2 O 3 grains. The results revealed that the addition of Fe element significantly enhances the crystallization process of mullite in alumina-mullite fibers. Specifically, adding iron sol resulted in the reduce of α-Al 2 O 3 formation temperature to 1300 °C, while introducing Ferric nitrate solution promoted the formation of mullite phase. Simultaneous introduction of 1.3 wt% iron sol and 1.3 wt% Ferric nitrate solution contributed to achieve alumina-mullite fiber with tensile strength of 2.06 GPa. In addition, the influence mechanism of Fe source on the phase transformation and microstructures of alumina-mullite fiber were discussed. [ABSTRACT FROM AUTHOR]