Significant phonon assignments in multiferroic BiFeO3 single crystal.
- Source :
-
Solid State Communications . Apr2024, Vol. 381, pN.PAG-N.PAG. 1p. - Publication Year :
- 2024
-
Abstract
- In the present work, the technique of Back Scattering Micro-Raman was employed at low and room temperatures in order to examine all the possible phonon vibration modes present in a crystal of BiFeO 3 (BFO). The observation & identification of all E (TO), E (LO), A1 (TO), and A1 (LO) normal modes was sucessfully accomplished. The low temperature Raman spectroscopy measurements showed two one-magnon branches, σ-magnon at 20.06 cm−1 and γ-magnon at 26.93 cm−1. The spectral characteristics of the three A1 (LO) modes were observed at roughly 176.63 cm−1, 225.93 cm−1 and 505.53 cm−1, exhibiting low intensity longitudinal optical modes. The observed peaks at 145.34 cm−1, 223.92 cm−1, 292.54 cm−1, and 552.18 cm−1 were identified and categorized as A1 (TO) modes. E (TO) peaks were observed at 73.30 cm-1, 131.94 cm-1, 239.35 cm-1, 265.04 cm-1, 278.45 cm-1, 349.95 cm-1, 374.69 cm-1, 441.04 cm-1, 522.99 cm-1. In addition, E(LO) peaks were observed at 80.76 cm-1, 175.03 cm-1, 241.59 cm-1, 275.42 cm-1, 346.92 cm-1, 371.34 cm-1, 419.38 cm-1, and 469.65 cm-1. • Micro-Raman Backscattering Technique was used. • E(TO), E(LO), A1(TO) and A1(LO) normal modes were assigned. • σ-magnon and ϒ-magnon were observed at 20.06 cm-1 and at 26.93 cm-1, respectively. • A1(LO) modes were observed at 176.63 cm-1, 225.93 cm-1 and 505.53 cm-1. • A1(TO) modes were observed at 145.34 cm-1, 223.92 cm-1, 292.54 cm-1 and 552.18 cm-1. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00381098
- Volume :
- 381
- Database :
- Academic Search Index
- Journal :
- Solid State Communications
- Publication Type :
- Academic Journal
- Accession number :
- 175412105
- Full Text :
- https://doi.org/10.1016/j.ssc.2023.115398