Ni–CoP catalyst for efficient and robust NaBH4 hydrolysis.

Hydrogen fuel is a non-toxic and source-abundant energetic system, but for its applications in the industry, several issues related to its storage must be resolved. Compounds like NaBH 4 appear as promising hydrogen sources, while can release the latter rapidly under controllable conditions with the use of heterogeneous catalyst systems. In this work, we synthesized a Ni–CoP catalyst by electrodeposition in a three-step process on carbon paper as support. The materials were characterized via SEM-EDS, XRD, and XPS techniques, while the hydrogen evolution reaction (HER) from alkaline NaBH 4 solutions was tested as a batch experiment. Ni–CoP catalyst showed a high amount of H 2 generated in a short time (∼550 mL in 1 min) and remained at 78 and 54% of its initial performance after respectively 100 and 300 h of a continuous hydrolysis process. Our catalyst revealed exceptional performance and stability at higher temperatures and a long process time, which have been a rare subject of investigation in other reports for NaBH 4 hydrolysis in the past. This work paves a new perspective in studying catalysts for hydrogen generation from borohydrides. [Display omitted] • Ni–CoP catalyst was electrodeposited on a carbon support. • Material characterization proved the formation of desired active layers. • High efficiency and stability of the catalyst for a long-term NaBH 4 hydrolysis was revealed. [ABSTRACT FROM AUTHOR]