Preparation of a Gradient Anti-Oxidation Coating for Aircraft C/C Composite Brake Disc and Its High-Temperature In Situ Self-Healing Performance.

We studied a gradient anti-oxidation coating of C/C composite materials for aircraft brake discs with a simple process and low costs. The gradient coating consists of two layers, of which the inner layer is prepared with tetraethyl orthosilicate (Si (OC2H5)4), C2H5OH, H3PO4 and B4C, and the outer layer is prepared with Na2B4O7.10H2O, B2O3, and SiO2 powder. The experimental results show that after being oxidized at 700 °C for 15 h, the oxidation weight loss of the sample with the coating was only −0.17%. At the same time, after 50 thermal cycles in air at 900 °C, the sample's oxidation weight loss was only −0.06%. We conducted the 1:1 dynamic simulation test for aircraft brake discs, and the brake disc did not oxidize, thus meeting the requirements for aircraft use. In addition, the anti-oxidation mechanism of the coating was analyzed via scanning electron microscopy (SEM), X-ray diffraction (XRD), differential thermal analysis (DSC-TGA), and high-temperature in situ SEM. [ABSTRACT FROM AUTHOR]