Effect of Boron Content in LiOH Solutions on the Corrosion Behavior of Zr-Sn-Nb Alloy.

In pressurized water reactors, LiOH may be concentrated in some areas, leading to the accelerated corrosion of fuel claddings. Injecting boric acid into primary coolants can mitigate the accelerated corrosion effect of LiOH on Zircaloys, but the effects of boron content on the corrosion behavior of the Zr-Sn-Nb alloy are still unknown. This work focused on the corrosion and hydrogen absorption behavior at 360 °C/18.6 MPa in 100 mg/kg LiOH solutions with 0 mg/kg, 50 mg/kg, and 200 mg/kg boron contents for up to 510 days, aiming to study the effect of boron content on corrosion resistance in LiOH solutions. Corrosion kinetics, microstructures of oxide films, hydrogen absorption concentrations and hydride morphology were obtained after the test. The results show that injecting boron in LiOH solutions can significantly reduce the corrosion weight gain, hydrogen concentration, and hydrogen length of Zr-Sn-Nb alloys, that is, improving corrosion resistance effectively. During the oxidation of the Zr-Sn-Nb alloy, B3+ and Li+ incorporate in oxide films. The incorporation of Li+ may lead to the generation of oxygen vacancies, which can carry oxygen from the solutions to O/M interface, accelerating corrosion. The incorporation of B3+ in oxide films will slow down the oxidation of Zr-Sn-Nb alloys by reducing the oxygen vacancies caused by Li+ aggregation. [ABSTRACT FROM AUTHOR]