Al2O3 fiber-reinforced MAX phase ceramic matrix composite.
- Source :
-
Ceramics International . Jul2024, Vol. 50 Issue 14, p25400-25411. 12p. - Publication Year :
- 2024
-
Abstract
- In the aerospace industry, lightweight can reduce the weight of the engine and improve the thrust-weight ratio of the engine. Ceramic matrix composites have attracted widespread attention in the industry due to their much lower density compared to high-temperature alloys and excellent high-temperature performance. SiC fiber-reinforced SiC ceramic matrix composites are the most outstanding representatives, but their long manufacturing cycle and high manufacturing costs limit their widespread use. Ti 2 AlC is a new type of ceramic material with the characteristics of low density, high melting point, high-temperature resistance, oxidation resistance, and corrosion resistance of ceramic materials, as well as the conductivity and machinability of metals. However, its mechanical properties are slightly inadequate. The use of chopped fibers for toughening can compensate for these deficiencies to a certain extent and improve mechanical properties. This article first explored the influence of various process parameters on the mechanical properties of pure-phase Ti 2 AlC ceramic materials in SPS preparation technology and then prepared Ti 2 AlC composites reinforced with 10 vol%, 20 vol%, and 30 vol% Al 2 O 3 chopped fibers. The results showed that the samples prepared at 1300 °C, 40 MPa, and 10 min had a flexural strength of 697 MPa and a fracture toughness of 9.83 MPa m1/2 when the volume ratio of the reinforcement phase was only 10 vol%, which was the same as that of the continuously fiber-reinforced SiC f /SiC composites. This study showed that the MAX phase matrix composites reinforced with chopped fibers have the potential to become high-temperature structural materials by adjusting the composite composition and optimizing the preparation process. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 50
- Issue :
- 14
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 177630162
- Full Text :
- https://doi.org/10.1016/j.ceramint.2024.04.272