Surface Modification of Feldspathic Ceramic Used for Minimally Invasive Restorations: Effect of Airborne Particle Type on the Surface Properties and Biaxial Flexural Strength.

This study aimed to evaluate the effect of airborne particle abrasion with different particles on the surface free energy, roughness, and biaxial flexural strength of a feldspathic ceramic by comparing it with hydrofluoric acid etching, the standard surface treatment, and polishing. Square-shaped feldspathic ceramic specimens (12 mm × 12 mm × 1.2 mm) were divided into subgroups as airborne particles abraded with alumina (AO3a, AO3b, AO25, AO50a, AO50b, AO90, AO110a, AO110b, AO120a, and AO120b), silica (SO50a, SO50b, SO100, and SO100/200), or nutshell granule (NS100/200), hydrofluoric acid etched, and polished (n = 12). Surface free energy (n = 5), roughness (n = 5), biaxial flexural strength (n = 12), and Weibull moduli (n = 12) were investigated. Data were evaluated with 1-way ANOVA and Tukey HSD tests, and possible correlations were investigated with Pearson's correlation (α = 0.05). SO100/200 mostly had lower surface free energy (p ≤ 0.011), and polishing and etching led to higher surface free energy than AO3a, AO3b, and AO120a (p ≤ 0.031). Polished, SO100, and SO50b specimens mostly had lower roughness and AO125 had the highest roughness (p ≤ 0.029). SO100/200 mostly had lower biaxial flexural strength (p ≤ 0.041), and etched specimens had higher biaxial flexural strength than AO120a, AO120b, and SO50b (p ≤ 0.043). AO3b had the highest (33.56) and AO120b had the lowest (11.8) Weibull modulus. There was a weak positive correlation between the surface free energy and the biaxial flexural strength (r = 0.267, p = 0.011). A larger particle size mostly resulted in higher roughness, which was also affected by the particle shape. Most of the test groups had similar biaxial flexural strength to that of the hydrofluoric acid-etched group. Therefore, for tested feldspathic ceramic, airborne particle abrasion with tested parameters may be a suitable alternative without causing any further damage. [ABSTRACT FROM AUTHOR]