An in vitro evaluation of the fatigue behavior of resin composite materials as part of a translational research cycle.

This study aimed to reproduce and translate clinical presentations in an in vitro set-up and evaluate laboratory outcomes of mechanical properties (flexural strength, fatigue resistance, wear resistance) and link them to the clinical outcomes of the employed materials in the Radboud Tooth Wear Project (RTWP). Four dental resin composites were selected. 30 discs (Ø12.0 mm, 1.2 mm thick) were fabricated for each of Clearfil TM AP-X (AP), Filtek TM Supreme XTE (FS), Estenia TM C&B (ES), and Lava Ultimate (LU). Cyclic loading (200 N, 2 Hz frequency) was applied concentrically to 15 specimens per group with a spherical steatite indenter (r = 3.18 mm) in water in a contact-load-slide-liftoff motion (105 cycles). The wear scar was analysed using profilometry and the volume loss was digitally computed. Finally, all specimens were loaded (fatigued specimens with their worn surface loaded in tension) until fracture in a biaxial flexure apparatus. The differences in volume loss and flexural strength were determined using regression analysis. Compared to AP and FS, ES and LU showed a significantly lower volume loss (p < 0.05). Non-fatigued ES specimens had a similar flexural strength compared to nonfatigued AP, while non-fatigued FS and LU specimens had a lower flexural strength (p < 0.001; 95 %CI: −80.0 – 51.8). The fatigue test resulted in a significant decrease of the flexural strength of ES specimens, only (p < 0.001; 95 %CI: −96.1 – −54.6). These outcomes concur with the outcomes of clinical studies on the longevity of these composites in patients with tooth wear. Therefore, the employed laboratory test seems to have the potential to test materials in a clinically relevant way. [ABSTRACT FROM AUTHOR]