Effect of Ta on the tribological behavior of in-situ TiC/Ni composites.

The tribological behavior of TiC/Ni composites is optimized by adding Ta, due to the improved oxidation resistance and hardness. The (Ti,Ta)C particles with core-rim structure are formed, and particle size decreases from 1.03 µm to 0.75 µm by adding 8 wt% Ta, and the hardness increases from 630.43 HV to 669.13 HV. At 20 N load, the primary wear mechanism is oxidation wear and the tribological property is influenced by oxidation resistance. At 50 N load, the main wear mechanism includes abrasive, adhesive, delamination and oxidation wear, and the tribological behavior is mainly influenced by the hardness and oxidation resistance. [ABSTRACT FROM AUTHOR]