Self‐crossing hyaluronic acid filler with combination use of polydioxanone thread in minipig model.

Introduction: The advances of self‐crossing hyaluronic acid (SC‐HA) fillers combination use with polydioxanone thread in minipigs were examined for compatibility, effectiveness, and immune response. Materials and Methods: A 12‐week experiment was conducted using 6 minipigs (3 male and 3 female each) to evaluate the effects of SC‐HA filler. The molecular weight of SC‐HA filler was fixed at 200 kDa and alternative storage modulus of G80, G250, and G500 were examined. The procedure involved injecting SC‐HA filler and polydioxanone threads into the skin tissue of anesthetized minipigs, and tissue sampling after 1 month (three minipigs), and 3 months (three minipigs) for histological staining and analysis. The immune reaction was observed during the experiment. Results: The practitioner reported it was easy to inject the SC‐HA filler in combination with polydioxanone threads. All four storage modulus of SC‐HA fillers were injectable within the polydioxanone thread containing cannula. Also, during the procedure, there were no immune responses at the treated sites. The results of the histological tissue examination confirmed that there was no chemical interaction between SC‐HA filler and the existing polydioxanone thread, and it was observed that SC‐HA filler was more uniformly distributed within the tissue with lower storage modulus, resulting in a higher production of collagen in the surrounding filler. When combined with scaffold polydioxanone thread, the scaffold polydioxanone thread helped spread the filler evenly, resulting in a more evenly distributed collagen around the filler. Conclusion: Today, the combination therapy of filler and polydioxanone thread in one procedure is challenging due to the high viscosity of conventional fillers. However, this study confirmed that combination therapy of filler and polydioxanone thread is possible with SC‐HA fillers. Additionally, it was found that polydioxanone thread does not seem to interfere with the crosslinking reaction of SC‐HA filler, and if used with a higher pH of polydioxanone, it may enhance the cross‐linking reaction and achieve a higher viscosity value. Finally, the study resulted in the idea of concrete as SC‐HA filler and reinforcing rod for polydioxanone thread. [ABSTRACT FROM AUTHOR]