Experimental characterization of epoxy/quartz composite material exposed to PDs.

• Epoxy resin-based composite insulator degrades when exposed to partial discharges (PDs); • PDs activity led to partial or total erosion of epoxy resin; • air-plasma action can trigger chemical reactions on the surface of epoxy resin; • CO 2 -plasma causes only erosion effects. Failures due to the degradation of polymeric insulation in components of electrical power systems are difficult to predict. Partial discharges (PDs) are one of the main phenomena that contribute to polymeric insulators' aging. Therefore, a better understanding of the aging process due to PDs is crucial to develop effective models that predict degradation, optimize materials and propose diagnostic indicators. Here we present an experimental characterization, via Fourier-transform Infrared spectroscopy (FTIR), of a composite material exposed to PDs. The material consisted of cured epoxy resin mixed with silica (quartz). Aging tests with surface discharges, using a needle-plate configuration, were conducted considering two atmospheres (air and CO 2) and four exposition times (6, 24, 72 and 120 hours). To aid the interpretation of spectroscopic data, we included a series of simulation results. The main effect observed was the erosion and removal of epoxy resin from the surface of the samples, proportionally to treatment time and distance from the needle. Along with erosion, new chemical species (possibly oxalate salts) were detected on the surface exposed to air-plasma. These species were likely formed and then removed due to plasma activity over time. On the other hand, samples aged in CO 2 atmosphere underwent only epoxy resin erosion. [ABSTRACT FROM AUTHOR]