Enhanced Magnetocaloric Properties of the (MnNi) 0.6 Si 0.62 (FeCo) 0.4 Ge 0.38 High-Entropy Alloy Obtained by Co Substitution.

In order to improve the magnetocaloric properties of MnNiSi-based alloys, a new type of high-entropy magnetocaloric alloy was constructed. In this work, Mn0.6Ni1−xSi0.62Fe0.4CoxGe0.38 (x = 0.4, 0.45, and 0.5) are found to exhibit magnetostructural first-order phase transitions from high-temperature Ni2In-type phases to low-temperature TiNiSi-type phases so that the alloys can achieve giant magnetocaloric effects. We investigate why chexagonal/ahexagonal (chexa/ahexa) gradually increases upon Co substitution, while phase transition temperature (Ttr) and isothermal magnetic entropy change (ΔSM) tend to gradually decrease. In particular, the x = 0.4 alloy with remarkable magnetocaloric properties is obtained by tuning Co/Ni, which shows a giant entropy change of 48.5 J∙kg−1K−1 at 309 K for 5 T and an adiabatic temperature change (ΔTad) of 8.6 K at 306.5 K. Moreover, the x = 0.55 HEA shows great hardness and compressive strength with values of 552 HV2 and 267 MPa, respectively, indicating that the mechanical properties undergo an effective enhancement. The large ΔSM and ΔTad may enable the MnNiSi-based HEAs to become a potential commercialized magnetocaloric material. [ABSTRACT FROM AUTHOR]