Enhanced photocatalytic degradation of harmful pollutants by MoO3/SiO2/MXene nanocomposite powder catalyst.

The search for materials to treat wastewater is especially crucial. Herein, we have prepared 1D molybdenum oxide (MoO 3) nanobelts through a hydrothermal approach. The binary (MoO 3 /SiO 2) and ternary composites of MoO 3 /SiO 2 /MXene were synthesized via ultrasonication route. The as-prepared MoO 3 , MoO 3 /SiO 2, and MoO 3 /SiO 2 /MXene composites were employed to investigate the photocatalytic behavior of two organic dyes, methyl orange (MO) and crystal violet (CV). The % degradation of MO in the presence of MoO 3 nanobelts and MoO 3 /SiO 2 was calculated to be 48.9 % and 74.4 %, respectively. In the case of CV dye, the degradation (%) was observed at 53.7 % and 75.9 %. The MoO 3 /SiO 2 /MXene composite revealed the best photocatalytic behavior against both MO and CV dyes by removing 94.7 % and 97.7 % under visible light irradiation. The rate constant values of MoO 3 nanobelts, MoO 3 /SiO 2 and MoO 3 /SiO 2 /MXene composite for MO dye were calculated to be 0.00568 min−1, 0.01156 min−1, and 0.02399 min−1 and for CV dye 0.00679 min−1, 0.01208 min−1, and 0.02798 min−1 respectively. A scavenging test was carried out to monitor the main photo-active species that take part during the photocatalysis and hydroxyl radicals were found to be the highly active species during whole photodegradation progression. The SiO 2 particles function as a good adsorbent medium and transfer the adsorbed organics toward more active sites to advance the reaction. 2D MXene nanosheets, as good conductors, reduce the recombination rate of charges, offer large surface area, and facilitate fast transfer of charges. The results suggest that MoO 3 /SiO 2 /MXene composite is a potential contender for wastewater remediation applications. [Display omitted] • Ternary composite (MoO 3 /SiO 2 /MXene) was synthesized using an ultrasonication approach, with a crystallite size of 19.48 nm. • SEM analysis confirmed the successful synthesis of MoO 3 nanobelts and their ternary composite with SiO 2 and MXene sheets. • The synthesized samples were utilized for the photodegradation of two organic dyes, Crystal Violet and Methyl Orange. • The MoO 3 /SiO 2 /MXene nanocomposite demonstrated the highest photocatalytic activity against both dyes. [ABSTRACT FROM AUTHOR]