Electrochemical Performance of LiTa 2 PO 8 -Based Succinonitrile Composite Solid Electrolyte without Sintering Process.

Solid-state batteries (SSBs) have been widely studied as next-generation lithium-ion batteries (LiBs) for many electronic devices due to their high energy density, stability, nonflammability, and chemical stability compared to LiBs which consist of liquid electrolytes. However, solid electrolytes exhibit poor electrochemical characteristics due to their interfacial properties, and the sintering process, which necessitates high temperatures, is an obstacle to the commercialization of SSBs. Hence, the aim of this study was to improve the interfacial properties of the lithium tantalum phosphate (LTPO) solid electrolyte by adding succinonitrile (SN) on the interface of the LTPO particle to enhance ionic conductivity without the sintering process. Electrochemical impedance spectroscopy (EIS), the Li symmetric cell test, and the galvanostatic cycle test were performed to verify the performance of the SN-containing LTPO composite electrolyte. The LTPO composite solid electrolyte exhibited a high ionic conductivity of 1.93 × 10−4 S/cm at room temperature (RT) compared to the conventional LTPO. Also, it showed good cycle stability, and low interfacial resistance with Li metal, ensuring electrochemical stability. On the basis of our experimental results, the performance of solid electrolytes could be improved by adding SN and lithium salt. In addition, the SN can be used to fabricate the solid electrolytes without the sintering process at high temperatures. [ABSTRACT FROM AUTHOR]