Magnetic Domain and Structural Defects Size in Ultrathin Films.

Herein, a model is proposed for measuring the structural defects size r0 in an ultrathin magnetic layer with perpendicular magnetic anisotropy. Based on the observations of magnetic domains in Ta/Pt/Co/Pt ultrathin films, using polar magneto‐optical Kerr effect microscopy and measurements of their magnetic anisotropies, the correlation between magnetic domains size D and structural defects size r0, as well as the defects concentration parameter αK, which designates the degree of pinning, has been modeled. The average r0 value found is high in the sample with unannealed buffer layers and considerably decreases with annealing. It is 6.17 nm with unannealed Ta/Pt buffer layers, 1.06 nm in sample with Ta/Pt buffer layers annealed at 423 K, and 0.49 nm in that with buffer layers annealed at 573 K. The significant drop of r0 is in good agreement with the high depinning noted with buffer layers annealing in recent work. [ABSTRACT FROM AUTHOR]