Structure, dielectric, and magnetic properties of Sr2TiMnO6 ceramics.

Sr2TiMnO6, a double perovskite associated with high degree of B-site cation disorder was investigated in detail for its structural, magnetic, and dielectric properties. Though x-ray powder diffraction analysis confirms its cubic structure, first order Raman scattering and infrared reflectivity spectra indicate a breaking of the local cubic symmetry. The magnetization study reveals an anomaly at 14 K owing to a ferrimagnetic/canted antiferromagneticlike ordering arising from local Mn-O-Mn clusters. Saturated M-H hysteresis loops obtained at 5 K also reflect the weak ferromagnetic exchange interactions present in the system and an approximate estimation of Mn3+/Mn4+ was done using the magnetization data for the samples sintered at different temperatures. The conductivity and dielectric behavior of this system has been investigated in a broad temperature range of 10 to 300 K. Intrinsic permittivity was obtained only below 100 K whereas giant permittivity due to conductivity and Maxwell-Wagner polarization was observed at higher temperatures. X-ray photoemission studies further confirmed the presence of mixed oxidation states of Mn and the valence band spectra analysis was carried out in detail. [ABSTRACT FROM AUTHOR]