Preparation of cobalt–zinc ferrite (Co0.8Zn0.2Fe2O4) nanopowder via combustion method and investigation of its magnetic properties

Abstract: Cobalt–zinc ferrite (Co0.8Zn0.2Fe2O4) was prepared by combustion method, using cobalt, zinc and iron nitrates. The crystallinity of the as-burnt powder was developed by annealing at 700°C. Crystalline phase was investigated by XRD. Using Williamson–Hall method, the average crystallite sizes for nanoparticles were determined to be about 27nm before and 37nm after annealing, and residual stresses for annealed particles were omitted. The morphology of the annealed sample was investigated by TEM and the mean particle size was determined to be about 30nm. The final stoichiometry of the sample after annealing showed good agreement with the initial stoichiometry using atomic absorption spectrometry. Magnetic properties of the annealed sample such as saturation magnetization, remanence magnetization, and coercivity measured at room temperature were 70emu/g, 14emu/g, and 270Oe, respectively. The Curie temperature of the sample was determined to be 350°C using AC-susceptibility technique. [ABSTRACT FROM AUTHOR]