Exchange bias and enhanced coercivity in phase separated La0.45Sr0.55MnO3 and Pr0.55(Ca0.65S0.35)0.45MnO3 films.
- Source :
-
Journal of Applied Physics . Dec2011, Vol. 110 Issue 12, p123907. 5p. 5 Graphs. - Publication Year :
- 2011
-
Abstract
- An epitaxial La0.45Sr0.55MnO3 (LSMO) film, which has a paramagnetic-to-ferromagnetic transition at ∼260 K and a partial ferromagnetic-to-antiferromagnetic transition at ∼150 K upon cooling, was synthesized on (001) (La0.18Sr0.82)(Al0.59Ta0.41)O3 with pulsed laser deposition. The x-ray diffraction pattern showed interference fringes around the (002) LSMO peak, indicating a successful growth of a high quality and smooth film. When the LSMO film was cooled down in a magnetic field of 5 kOe, it exhibited a large exchange bias (HEX) of ∼490 Oe and an enhanced coercivity (HC) of ∼800 at 10 K, respectively. The observed exchange bias effect, which is associated with phase coexistence of the ferromagnetic (FM) and antiferromagnetic (AF) phases, displayed a distinctive training effect, which is probably due to a competing spin order at the boundary between the FM and AF phases. Similarly, we also observed a large exchange bias and enhanced coercivity in a phase separated Pr0.55(Ca0.65S0.35)0.45MnO3 film, which had simultaneous FM and AF transitions at ∼150 K. Our results show that the exchange bias effect can be induced even in single layer films with a magnetic phase coexistence state of FM and AF phases, which may be exploited as a very simple structure for spin-valve devices. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00218979
- Volume :
- 110
- Issue :
- 12
- Database :
- Academic Search Index
- Journal :
- Journal of Applied Physics
- Publication Type :
- Academic Journal
- Accession number :
- 70097483
- Full Text :
- https://doi.org/10.1063/1.3666023