Agar-Based Gel Electrolyte for Electrochromic Device Application.

Gel Polymer Electrolytes (GPE) based on agar and containing LiClO4 have been prepared, characterized and applied to electrochromic devices. The ionic conductivity revealed the best result of 6.5 × 10−5 S/cm for the sample with 17 wt.% of LiClO4, which increased to 5.4 × 10−4 S/cm at 72°C. The GPE have been used in electrochromic devices (ECD) with K-glass/WO3/GPE/CeO2-TiO2/K-glass configuration. The ECD changed transmittance values up to 30% between the colored and transparent states. The charge density measurements revealed an increase of 5.5 to 7.5 mC/cm2 from the first to 500th cycles and then a decrease to 4.4 mC/cm2 during the next 4500 cycles. Coloration efficiency (η) of 25 cm2/C was obtained. [ABSTRACT FROM PUBLISHER]